Progress in Hot-Wire deposited nanocrystalline silicon solar cells

Autor/a

Fonrodona Turon, Marta

Director/a

Bertomeu i Balagueró, Joan

Tutor/a

Bertrán Serra, Enric

Fecha de defensa

2003-09-15

ISBN

8468836346

Depósito Legal

B.44130-2003



Departamento/Instituto

Universitat de Barcelona. Departament de Física Aplicada i Òptica

Resumen

The tendency towards cost reduction in the photovoltaic industry has led to the development of the so-called thin film silicon technology. Among the different possible morphologies, a material that presents very promising features is nanocrystalline silicon (nc Si:H), which consists in an aggregate of crystallites with sizes in the order of few tens of nanometers embedded in an amorphous matrix. The deposition technique used at Universitat de Barcelona to grow nc-Si:H solar cells is Hot-Wire Chemical Vapour Deposition (HWCVD), which features several advantages in comparison with Plasma Enhanced CVD, the most widely used one in industry at the moment (higher deposition rates, simpler and cheaper deposition geometry and easier to scale to large area deposition).<br/>In order to grow a completely Hot-Wire deposited nanocrystalline silicon solar cell with enhanced efficiency, different strategies have been followed. First of all, the effects of the different deposition parameters, especially the tantalum filament temperature, have been studied aiming to the obtaining of compact material. Several modifications of the set-up have also been performed with the same finality. Material with good structural, electrical and transport properties has been obtained at low filament temperature (1600ºC). Secondly, the effects of the substrate nature on the microstructure of the nc-Si:H layers has been considered in the three possible cases (intrinsic, n-type and p-type doped layers). Later on, the performance of different p-i-n solar cells has been studied. Firstly, the effects of different preliminary light trapping strategies has been considered: the use of a textured front contact and of a back reflector. Finally, the relation existent between the microsctructure of the material and the performance and stability of the devices has been investigated. Different degradation mechanisms that affected our devices were detected and their possible causes identified (contact degradation, effects outside the p-i-n nc Si:H structure, active layer degradation). <br/>A best efficiency of 5.2% in a completely Hot-Wire deposited p-i-n solar cell has been achieved at low filament (1600ºC) and substrate (200ºC) temperatures and by using preliminary light trapping strategies. Stability of this device was verified after more than 1000 hours of light soaking. The preliminary character of this device makes it a very promising starting point to further increase the conversion efficiency of Hot-Wire deposited nanocrystalline silicon solar cells.

Palabras clave

Cèl·lules fotovoltaiques; Silici nanocristal·lí; Tecnologia del silici

Materias

53 - Física

Área de conocimiento

Ciències Experimentals i Matemàtiques

Documentos

tesimfonrodona.pdf

4.489Mb

 

Derechos

ADVERTIMENT. L'accés als continguts d'aquesta tesi doctoral i la seva utilització ha de respectar els drets de la persona autora. Pot ser utilitzada per a consulta o estudi personal, així com en activitats o materials d'investigació i docència en els termes establerts a l'art. 32 del Text Refós de la Llei de Propietat Intel·lectual (RDL 1/1996). Per altres utilitzacions es requereix l'autorització prèvia i expressa de la persona autora. En qualsevol cas, en la utilització dels seus continguts caldrà indicar de forma clara el nom i cognoms de la persona autora i el títol de la tesi doctoral. No s'autoritza la seva reproducció o altres formes d'explotació efectuades amb finalitats de lucre ni la seva comunicació pública des d'un lloc aliè al servei TDX. Tampoc s'autoritza la presentació del seu contingut en una finestra o marc aliè a TDX (framing). Aquesta reserva de drets afecta tant als continguts de la tesi com als seus resums i índexs.

Este ítem aparece en la(s) siguiente(s) colección(ones)